The bright nickel layer on the stainless steel pipe is a silver white metal with slight yellow light. Its hardness is higher than that of copper zinc, tin, cadmium, gold and silver, but lower than that of chromium and rhodium. Bright nickel has high chemical stability in air and good stability to alkali. Using Brightener on stainless steel pipe bright nickel can be directly plated without polishing, so as to improve the hardness, wear resistance and leveling of the surface, make the appearance of stainless steel pipe consistent with other nickel plated parts, and avoid the corrosion of potential difference between stainless steel pipe and other bright nickel. After using bright nickel solution for a period of time, due to the of brightenerGood ductility, used for forming products. It can also be machined to harden rapidly. Good weldability. Wear resistance and fatigue strength are better than stainless steel.Smalyavichy,Price of stainless steel pipe with mm diameter: according to the current market situation, the price of stainless steel pipe with mm diameter is yuan per ton.For example, the price of tons of goods = tons = the result example: the price excluding tax of ton of goods = a ton = ~ the total weight of the known coil weight and price = the coil weight price the thickness of stainless steel plate & Chi; Width & Chi; Long & Chi; e.g. & Chi; Χ Χ = kg stainless steel plate weight per square meter (kg) calculation formula: specific gravity thickness (mm) width (mm) length (m) stainless steel weight per meter (kg) stainless steel pipe calculation formula: diameter (mm) diameter (mm) (correct calculation of the price difference between burr and trimming of nickel stainless steel . chromium stainless steel) in the market, the price difference between burr and trimming of stainless steel is usually set at a fixed price. For example, it is generally considered in the market that the price difference between burr and trimming of is yuan tons and that of is yuan tons. In fact, this method is not scientific. In fact, the price difference between burr and trimming of stainless steel is different The correct calculation should be like this.Mandurah,Proper heat treatment process can prevent intergranular corrosion and obtain excellent corrosion resistance.Standard classification - classification: national standard GB industry standard Yb local standard enterprise standard qcb- classification: product standard packaging standard basic standard - standard level (divided into three levels): y level: international advanced level I level: international general level H level: domestic advanced level - national standard: stainless steel bar (level I) gb- stainless welding disc Park (level H)Rockwell hardness the Rockwell hardness test of stainless steel pipe is the same as Brinell hardness test. The difference is that it measures the depth of indentation. Rockwell hardness test is widely used at present, and HRC is second only to Brinell hardness Hb in steel pipe standards. Rockwell hardness can be used to measure metal materials from very soft to very hard, which makes up for the disadvantage of Brinell method, It is simpler than Brinell method and can read the hardness value directly from the dial of the hardness machine. However, due to its small indentation, the hardness value is not as accurate as Brinell method.

First of all, steel that will not rust is called stainless steel, but in an academic sense, steel resistant to weak corrosive media such as air, steam and water and chemical corrosive media such as acid, the steel resistant to weak corrosion medium is often called stainless steel, while the steel resistant to chemical medium is called acid resistant steel. Due to the difference in chemical composition between the two, the former is not necessarily resistant to chemical medium corrosion, while the latter is generally stainless. The corrosion resistance of stainless steel depends on the alloying elements contained in the steel. Chromium is the basic element for stainless steel to obtain corrosion resistance. When the chromium content in the steel reaches about %, chromium reacts with oxygen in the corrosive medium to form a thin oxide film (self passivation film) on the steel surface,SmalyavichySUS444 stainless steel, which can prevent further corrosion of the steel matrix. In addition to chromium, the commonly used alloy elements include nickel, molybdenum, titanium, niobium, copper, nitrogen etc., so as to meet the requirements of various uses on the microstructure and properties of stainless steel.The internal and external greasy dirt and sundries at the pipe end shall be completely removed to keep the pipe inside the pipe fittings clean.The back side is not protected by argon, and the flux coated welding wire (self protective flux cored welding wire) + TIG process is adopted. In the s, the backing welding wire has been developed. Recently, China has also developed the stainless steel backing welding wire (i.e. flux coated welding wire, such as tgftgftgftgf, etc.) It has been applied to the actual construction and achieved good results. We have successfully applied it in the capacity expansion and reconstruction project of Urumqi Petrochemical.quality index, ferritic stainless steel pipe has low-temperature brittleness like carbon steel, but austenitic steel does not. Therefore, while austenitic stainless steel or nickel base alloy does not show low-temperature brittleness. Sus (Cr) and SUS (cr) of ferritic stainless steel pipe It shows that the impact value decreases sharply at low temperature. Therefore, it is necessary to pay special attention when using at low temperature. As a way to improve the impact toughness of ferritic series stainless steel, high purification process can be considered. With the help of C and N level, the embrittlement temperature is in the range of - ℃ to - ℃Formula for hydraulic test pressure of stainless steel welded pipe for weight calculation fluid (gbt-): where: P - test pressure MPa; R - stress, taking yield point of %, MPa; s - nominal wall thickness of steel pipe, mm; D - Nominal outer diameter of steel pipe, mm.Stress relief treatment. Stress relief treatment is a heat treatment process to eliminate the residual stress of steel after cold working or welding. It is generally heated to ~ ℃ for tempering. For steels without stabilizing elements Ti and Nb, the heating temperature shall not exceed ℃, so as to avoid intergranular corrosion caused by chromium carbide precipitation. For cold worked and welded parts of ultra-low carbon and stainless steel containing Ti and Nb, they need to be heated at ~ ℃ and then cooled slowly to eliminate stress (the upper limit temperature is taken for eliminating welding stress), which can reduce the tendency of intergranular corrosion and improve the stress corrosion resistance of steel.

Bidirectional Product Description: the tensile strength of the material is ~ mpa, and the high working temperature can reach ℃.management,Stainless steel pipe factory stainless steel products are widely used in hardware products, furniture, mechanical structure, mechanical accessories, precision medical instruments, fluid transmission pipelines, such as furniture, medical oil, natural gas, water, gas, steam and other industries.[hot rolled strip / sheet] has the advantages of low hardness, easy processing and good ductility.At present, stainless steel backing is divided into two processes: back argon filling and non argon filling. Back argon filling protection can be divided into solid wire + TIG process and solid wire + TIG + water-soluble paper process; The back non argon filling protection is also divided into flux cored wire backing welding and welding rod (flux coated wire) backing TIG welding.Smalyavichy,Rockwell hardness the Rockwell hardness test of stainless steel pipe is the same as Brinell hardness test. The difference is that it measures the depth of indentation. Rockwell hardness test is widely used at present, and HRC is second only to Brinell hardness Hb in steel pipe standards. Rockwell hardness can be used to measure metal materials from very soft to very hard,SmalyavichyStainless steel pipe bending, which makes up for the disadvantage of Brinell method,SmalyavichyR13 stainless steel plate, It is simpler than Brinell method and can read the hardness value directly from the dial of the hardness machine. However, due to its small indentation the hardness value is not as accurate as Brinell method.The shape of pipe end stainless steel pipe can be divided into smooth pipe and threaded pipe (threaded steel pipe) according to the state of pipe end. Threading pipe can also be divided into ordinary threading pipe (pipe for conveying low pressure such as water and gas, which is connected by ordinary cylindrical or conical pipe thread) and special threaded pipe (pipe for petroleum and geological drilling, which is connected by special thread for important threading pipe). For some special pipes, in order to make up for the impact of thread on the strength of pipe end, the pipe end is usually thickened before threading (inner thickening, outer thickening or inner and outer thickening).AUSTENITIC FERRITIC duplex stainless steel on the basis of austenitic stainless steel, and cooperate with remelting treatment. High prices, various specifications of stainless steel plates, stainless steel coils, stainless steel belts and stainless steel tubes are supplied in time and cost-effective. It has become the preferred brand for many wire products. Welcome to buy! Stainless steel with duplex structure of austenite and ferrite (including ~ % & Delta; - ferrite) can be obtained. Typical steel grades include crniti, CrNiTi, ocrnimoti, etc. Duplex stainless steel has good weldability, no heat treatment is required after welding, and its tendency of intergranular corrosion and stress corrosion is also small. However, due to the high Cr content, it is easy to form & sigma; Pay attention when using.