Raw materials -- strip splitting -- welded pipe making -- heat treatment -- Correction -- straightening -- end repair -- pickling -- Hydrostatic Test -- Inspection (spray printing) - packaging -- delivery (warehousing) (pipes for welded pipe industrial piping).Austenitic stainless steel has good resistance to uniform corrosion, but there are still the following problems in local corrosion resistance: intergranular corrosion of austenitic stainless steel. Austenitic stainless steel will have intergranular corrosion when it is kept warm at ~ ℃ or cooled slowly. The higher the carbon content, the greater the tendency of intergranular corrosion. In addition, intergranular corrosion also occurs in the heat affected zone of the weldment. This is due to the precipitation of Cr rich CrC on the grain boundary. The chromium poor area is formed in the surrounding matrix, which is caused by corrosion of the primary cell. This intergranular corrosion phenomenon also exists in the ferritic stainless steel mentioned above.Barahona, after deep drawing, small black spots and RI high imitation dging will also appear on the surface of the area with large deformation, which will affect the BQ attribute.The manufacturing and maintenance of equipment consume more than tons of stainless steel pipe. This kind of industry mainly adopts sanitary or grade stainless steel pipe. The sanitary seamless pipe made of imported sus and l can meet the special requirements of various media in the field of food and biopharmaceutical. Stainless steel has the advantages and good performance of stainless steel. It is widely used in kitchen equipment, workbench, utensils and medical instruments in the food industry The demand for tableware, towel hanging bracket and bracket of refrigerator in daily life is increasing.Livno,CE--“ Code for design of cold formed stainless steel structural parts & rdquo; And & ldquo; jointly published by nidi and euro inox; Structural stainless steel design manual & rdquo; The design of structural parts for buildings with long service life and good integrity has been simplified.Crimping: during crimping the convex part of the pipe fitting is placed in the concave groove of the die, and the jaw is perpendicular to the pipe axis.Model & mdash; It has better temperature resistance.

Model & mdash; Except that the risk of weld corrosion of the material is reduced due to the addition of titanium, other properties are similar. Stainless steel decorative pipe, stainless steel pipe, series stainless steel pipe & mdash; Ferritic and martensitic stainless steel model & mdash; Good heat resistance, weak corrosion resistance, % Cr, % Ni.The steady creep rate is usually used to evaluate the long-time creep performance of materials. For the application of long-life materials, the steady-state creep rate of stainless steel pipe under high temperature and stress is the key index of the material, and can be extrapolated. The following are the test results of stainless steel pipe under different test conditions. The results show that the steady-state creep rate of stainless steel pipe sample is in the order of magnitude after creep at ℃ (mpa ℃ (mpa) for h; when the temperature condition increases to ℃ (the stress decreases to MPa), and the steady-state creep rate is in the order of magnitude; when the temperature further increases to ℃ (the temperature creep rate of mpa stainless steel pipe sample increased to ℃ (mpa steady-state creep rate reaches the maximum value under several test conditions and creep fracture occurs. See for the change of steady-state creep rate of stainless steel pipe sample under several conditions. When the temperature increases, the material maintains a low level of creep rate. Under ℃ MPa, s creep deformation rate does not increase, which shows little influence on the temperature and stress, and creep fracture occurs under this condition Compared with several other common structural materials, it can be seen that the creep performance of several materials is better than that of ordinary materials under all test conditions. After hours of test, the total strain does not exceed .%. The curve is relatively stable and the fluctuation is small, indicating that the test data is stable and reliable. Stainless steel pipes are widely used because of their excellent corrosion resistance It is widely used in petrochemical industry, pipeline transportation and other working conditions with strong corrosive media. The main reason for the corrosion resistance of stainless steel pipes is the addition of a large number of elements CrNi, and Cr is the main element determining the corrosion resistance of stainless steel pipes. The electrode potential of stainless steel pipes jumps with the increase of Cr content. However, stainless steel pipes are in the subsequent heat treatment During the treatment, Cr element will precipitate into the matrix in the form of carbide. On the one hand, the hardness of Cr carbide is larger than that of the matrix, and the service wear process can improve the wear resistance of stainless steel pipe. On the other hand, the precipitation of Cr containing carbide will lead to Cr Element dilution zone in some parts of the matrix, increase the number of batteries of the material, reduce the electrode potential of stainless steel pipe and reverse the corrosion Therefore, the combination of mechanical properties and corrosion resistance of stainless steel pipe materials needs to be considered. At present, some scholars have studied the effects of austenitizing temperature and time, tempering temperature and time on the mechanical properties of stainless steel pipe by heat treatment to change the corrosion resistance of stainless steel pipe And corrosion resistance, it is found that austenitizing temperature can change mechanical properties, but has little effect on corrosion performance, while tempering temperature has a great effect on the corrosion resistance of materials. Appropriate austenitizing temperature and tempering temperature can improve the corrosion and wear resistance of materials. Some scholars use surface treatment to improve the corrosion and wear resistance of materials, It is concluded that low-temperature nitriding forms a diffusion layer on the surface of the material, improves the wear resistance of the material, interacts with Cr and chemically stable phase -fen to improve the corrosion resistance of the material.Corrosion resistance of decorative stainless steel pipe the price of different series of stainless steel materials varies greatly. The corrosion resistance of more economical materials can not meet the higher application requirements, and the improvement of corrosion resistance of stainless steel materials by simple chemical passivation is limited. On the other hand, the traditional passivation treatment containing chromium salt has been gradually eliminated, and the passivation treatment of stainless steel has turned to the direction of environmental friendliness. Recently, citric acid passivation and silicon treatment on stainless steel surface have become a new research direction. The former has environmental protection characteristics because its passivation solution component does not contain chromium salt. The latter has found that silicon coupling agent is chemically adsorbed on the metal surface to form a protective silicon film with cross-linked network structure. The length of discoloration time of samples after different surface treatments was compared by blue dot method, the corrosion rate of samples after different surface treatments was distinguished by brine immersion test and the salt spray resistance of samples after different surface treatments was distinguished by neutral salt spray test, The differences of pitting corrosion resistance and resistance to corrosive medium of samples after different surface treatment were compared by electrochemical test. The film thickness of silicon film was indirectly characterized by film weight test, and scanning electron microscope, energy spectrometer, X-ray diffraction X-ray photoelectron spectroscopy and total reflection Fourier transform infrared spectroscopy characterized the surface films of different surface treated samples, and analyzed the structural composition and corrosion resistance mechanism of different films. Professional stainless steel plate, stainless steel coil, stainless steel belt, high price, service on-site settlement, honest management! At present, there are few studies on the combination of citric acid passivation and silicon treatment of stainless steel. Therefore, silicon treatment and the combination of citric acid passivation and acid silicon system treatment, and discusses the corrosion resistance mechanism of different films on its surface, which can provide reference for the new direction of stainless steel surface treatment, It has certain practical guiding significance. The corrosion resistance and mechanism of chemical passivation, silicon treatment and composite treatment of martensitic stainless steel were studied in this paper. The comprehensive comparison of the research results shows that the corrosion resistance of stainless steel treated with different surface treatments is different. The corrosion resistance of the sample treated with silicon alone is better than that treated with traditional dichromate passivation. The corrosion resistance of the composite treated sample treated with citric acid passivation and acid silicon system is further enhanced than that treated with acid silicon system alone. The composite treatment of citric acid passivation and acid silicon system treatment has excellent corrosion resistance and environmental protection characteristics,Barahona63 stainless steel pipe, and is expected to replace the traditional dichromate passivation treatment. According to the film weight test results, the surface silicon film weight of the composite treated sample after citric acid passivation and acid silicon system treatment is lower than that of the sample after acid silicon system treatment alone, indicating that the excellent corrosion resistance of the composite film not only depends on the surface silicon film, but also benefits from its double-layer film structure.Inspection standard,When hoisting stainless steel pipes, public slings, such as hoisting belt and public collet number, shall be used. It is strictly prohibited to use steel wire rope to avoid scratching the surface; and when hoisting and placing, it shall prevent scratching caused by impact and collision. If there are surface scratches, electric arc traces and surface purification in the process of transportation, storage and processing, it must be completely cleaned polished with an angle grinder, and then polished Polishing with optical sheet or metallographic sandpaper.The back side is not protected by argon, China has also developed the stainless steel backing welding wire (i.e. flux coated welding wire the backing welding wire has been developed. Recently, such as tgftgftgftgf, etc.) It has been applied to the actual construction and achieved good results. We have successfully applied it in the capacity expansion and reconstruction project of Urumqi Petrochemical.Water preparation, storage, transportation, purification, regeneration seawater desalination and other water industry excellent materials. The demand is about tons.

The best way to improve the quality of stainless steel pipe fittings is to change the process from ingot to billet. Due to the improvement of continuous casting process, this has become a necessary means to improve product quality.quality,Rockwell hardness the Rockwell hardness test of stainless steel pipe is the same as Brinell hardness test. The difference is that it measures the depth of indentation. Rockwell hardness test is widely used at present, and HRC is second only to Brinell hardness Hb in steel pipe standards. Rockwell hardness can be used to measure metal materials from very soft to very hard, which makes up for the disadvantage of Brinell method, It is simpler than Brinell method and can read the hardness value directly from the dial of the hardness machine. However, due to its small indentation, the hardness value is not as accurate as Brinell method.Corrosion resistance most stainless steel products require good corrosion resistance. Stainless steel pipe is similar to class I and II tableware, kitchen, water heater, water dispenser, etc. Some foreign businessmen also test the corrosion resistance of products: use NaCl aqueous solution to warm to boiling. After a period of time, the solution is to drain, wash and dry, and determine the weight loss to determine the degree of corrosion.Model & mdash; Martensite (high strength chromium steel), good wear resistance and poor corrosion resistance.Barahona,Stainless steel pipe factory stainless steel products are widely used in hardware products, furniture, mechanical structure, mechanical accessories, precision medical instruments, fluid transmission pipelines, such as furniture, machinery, medical oil, natural gas, gas, steam and other industries.At the same time, the Ministry of construction attaches great importance to the application of stainless steel pipes. The industry standard of stainless steel water pipe was issued and implemented in . The Ministry of construction has issued documents on relevant technical specifications and installation sets of pipeline engineering, stainless steel coil, stainless steel belt and stainless steel pipe are qualified. Welcome to telephone inquiry and sincerely invite cooperation! At present, there are stainless steel pipes in Sichuan,BarahonaStainless steel mesh belt for food,Barahona316H stainless steel pipe, Guangdong, Zhejiang Jiangsu and other places, and the products have become mature. Therefore, the time for application has come.Refining and transportation industries are in great demand. Secondly, geological drilling, chemical industry, construction industry, machinery industry, aircraft and automobile manufacturing, boiler, medical equipment, furniture and bicycle manufacturing also need a large number of various steel pipes. With the development of new technologies such as atomic energy, rocket, missile and aerospace industry, stainless steel pipe plays an increasingly important role in national defense industry