In engineering, the following methods are often used to prevent intergranular corrosion: reduce the amount of carbon in steel so that the amount of carbon in steel is lower than the saturated solubility of austenite in equilibrium that is, fundamentally solve the problem of precipitation of chromium carbide (crc) on the grain boundary. Generally, the requirement of intergranular corrosion resistance can be met when the amount of carbon in steel is reduced to less than .%.Flux coated welding wire is used for backing welding, and argon gas is not used inside the weld. The welder's operation is simple and fastKizina,Surface treatment difference: surface treatment is usually divided into polishing, wire drawing and wire drawing, the cost per ton will increase by yuan.. Domestic wce cerium tungsten electrode is used for electrode data. The shape and diameter of the end of cerium tungsten electrode have a great impact on the fluctuation of welding process and weld formation.Harstad,Chloride ions exist in the service environment. Chloride ions exist widely, such as salt, sweat, sea water, sea breeze, soil, floating rust of iron foam and so on. Stainless steel corrodes rapidly in the presence of chloride ions, even more than ordinary low carbon steel. Therefore, there are requirements for the service environment of stainless steel, and it is necessary to remove dust frequently and keep it clean and dry. (in this way, we can give him a & ldquo; improper use & rdquo;) there is an example in the United States: an enterprise uses an oak container to contain a solution containing chloride ions. The container has been used for nearly years. The ninetieth generation of the last century plans to replace it. Because the oak material is not modern enough, the container leaks due to corrosion days after it is replaced with stainless steel.First of all, let's understand what stainless steel is. Generally speaking, steel resistant to weak corrosive media such as air, steam and water and chemical corrosive media such as acid, alkali and salt. Also known as stainless acid resistant steel. In practical application, the steel resistant to weak corrosion medium is often called stainless steel, while the steel resistant to chemical medium is called acid resistant steel. Due to the difference in chemical composition between the two, the former is not necessarily resistant to chemical medium corrosion while the latter is generally stainless. The corrosion resistance of stainless steel depends on the alloying elements contained in the steel. Chromium is the basic element for stainless steel to obtain corrosion resistance. When the chromium content in the steel reaches about %, chromium reacts with oxygen in the corrosive medium to form a thin oxide film (self passivation film) on the steel surface, which can prevent further corrosion of the steel matrix. In addition to chromium, the commonly used alloy elements include nickel, molybdenum,Kizina7cr17 stainless steel plate, titanium niobium, copper, nitrogen, etc., so as to meet the requirements of various uses on the microstructure and properties of stainless steel.Combined steel and spring steel, such as CrMnTi simn, (C content is expressed in ten thousandths).

Model & mdash; The corrosion resistance is the same, and the strength is better because the carbon content is relatively high.Since last year, foreign countries have frequently carried out & ldquo; Double inverse & rdquo; This has a great impact on China's stainless steel casting industry. Export is a large part of the development of China's stainless steel industry and occupies a huge market share in its industrial development. In the face of the current economic downturn and slow development speed, the development of China's stainless steel industry should continuously improve product quality, Better develop overseas trade and deal with trade protectionism, combine products with environmental protection, energy resources and cultural environment, and improve the competitiveness of stainless steel products. Only in this way can we achieve an invincible position in foreign trade.And stainless steel are molybdenum containing stainless steels. The molybdenum content of stainless steel is slightly higher than that of stainless steel. Due to the molybdenum content in stainless steel, the overall performance of this steel is better than that of and stainless steel. Under high temperature conditions, when the concentration is lower than % and higher than %, stainless steel has a wide range of applications. Stainless steel also has good chloride corrosion resistance, so it is usually used in marine environment.wholesaler,;- Ferromagnetism due to m transformation shall be considered in use (such as in instrument parts).Adjust the ratio of austenite forming elements to ferrite forming elements in the steel to make it have austenite + ferrite dual phase structure, in which ferrite accounts for % - %. This dual phase structure is not easy to produce intergranular corrosion.Inspection: after crimping, check the crimping size with a special gauge.

Model & mdash; General model; stainless steel. The GB brand is CrNi.Welcome calls ,When using this method, it should be noted that the water-soluble paper should be double-layer and must be pasted well,KizinaStainless steel seamless steel pipe, otherwise it is easy to cause damage and fall off of the water-soluble paper, resulting in loss of argon protection of the inner weld and oxidation, resulting in cutting of the weld junction and re welding, which can not ensure the welding quality and seriously affect the construction period. Therefore, the water-soluble paper should be strictly checked and pasted before welding.Corrosion fatigue resistant dual phase steel has high corrosion fatigue strength due to its high strength and corrosion resistance. Processing equipment is vulnerable to corrosive environment and loading cycle, and its characteristics are very suitable for such applications. The chemical composition of was determined after DEG/ ° After f ( & deg; / & deg; c) solid melt annealing, the ideal microstructure & alpha/ γ . If the temperature of heat treatment is higher than DEG; F, which may lead to the increase of ferrite composition. Like other duplex stainless steels, alloys are susceptible to intermetallic precipitation. Intermetallic phase at DEG; F and & deg; F, the precipitation rate is fast. Therefore, we need to test to ensure that there is no intermetallic phase. Refer to ASTM A for the test. For hot forming, we suggest that the forming should be at DEG; Below F. During hot forming treatment, the whole workpiece shall be heated as a whole, which shall be at DEG; F to & deg; F, and the alloy is very stable at this temperature. If the temperature is too high, the alloy is prone to hot tearing. Below this temperature, austenite will fracture. Below DEG; At F, the intermetallic phase will be formed quickly due to the influence of temperature and deformation. After hot forming, it should be immediately adjusted to DEG; F and quench to restore its phase balance toughness and corrosion resistance. We do not recommend stress relief, but if this is necessary, the material should be as low as & deg; F, followed by rapid cooling and water quenching.Only soluble paper or the combination of soluble paper and blocking plate is used for blocking ventilation protection (i.e. solid core welding wire + TIG + water-soluble paper)Kizina,Application field: tubular boiler for pipeline in harsh seabed environment product description: ultra (ultra) critical unit is the basis of modernization of power generation equipment and energy conservation and emission reduction. Among the important pressure parts of ultra (supercritical) boiler, superheater and reheater are the parts with high working temperature and bad working environment. Previously,Kizina304 stainless steel wire, all such materials used in China were imported from abroad, while only steel material manufacturers in the world have limited capacity. Such materials have a large gap, expensive import prices, which seriously affected the production of ultra supercritical boilers and the development of electric energy in China. At present, China's demand for utility boiler tubes is about tons, and with the continuous improvement of ultra (supercritical) power generation technology, the demand is expanding. Several large domestic enterprises have invested a lot of human and financial resources in the R & D and production of such products and have made considerable achievements. On the one hand, it has made its own contribution to the development of national electric power industry, but also brought considerable economic benefits to enterprises.Stainless steel pipe cost = actual thickness divided by thickness adjustment price + freight + processing fee. Coil price is switched to flat plate price = coil price actual thickness adjustment + leveling fee . Flat plate price is switched to coil price = plate price, thickness adjustment - leveling fee . Coil length = coil net weight . Coil width. Actual thickness including tax price algorithm = total weight of goods ( represents points, is points)Stainless steel pipe is durable and has been recognized by the engineering community, and relevant parties are starting from reducing the wall thickness and lowering the grid, so as to facilitate further development. In particular, the price of stainless steel pipe is not high, the reliability and price of pipe fittings are the main factors determining its development. Domestic developers have independently developed connection technology and pipe fittings in Sichuan, Guangdong, Zhejiang, Jiangsu and other places, which is a promising pipe. The Ministry of construction and relevant departments also attach great importance to this new type of pipe. According to China technology market management promotion center and gksz [] No. document on Application & ldquo; High diameter to wall ratio and high precision stainless steel medium and high pressure water supply pipes and supporting fittings and special technology & rdquo; It is learned from the notice that the application of stainless steel pipe technology and product is of great significance to improve the grade of modern buildings in China and improve and ensure the water quality of water supply.